Room-temperature multiferroicity in 2D ultrathin-layers and diversified magnetoelectric couplings

Peer-Reviewed Publication

Science China Press

Spin Distribution

image: The change of spin distribution and bandstructure upon FE switching for (a) Cu2(CrS2)3 and (b) Cu3(CrS2)4. Black and red arrows in the sketches of M-E loops denote the direction of polarization and magnetization, respectively. The smaller net magnetization marked by shorter red arrow in (b) is mainly attributed to the reduction in the magnetic moment of the top layer compared with other layers (left), which is "transferred" to the bottom of different spin direction after FE switching (right). Black and red lines in bandstructures denote spin-up and spin-down channel, respectively. view more 

Credit: ©Science China Press

The recent progress on two-dimensional (2D) van der Waals ferroelectrics may revolutionize the applications of ferroelectric (FE) materials in nanoelectronics. Their atomic-thickness renders high-density integration; their clean van der Waals interfaces allow for lattice mismatch, facilitating the epitaxial growth on various substrates including silicon; meanwhile many 2D materials are also high-mobility low-bandgap semiconductors. Predictions of intrinsic FE in several 2D materials have been experimentally confirmed, such as IV-VI group compound, In2Se3, van der Waals bilayer, Bi2O2Se, etc..

2D multiferroics with magnetoelectric (ME) couplings have also been explored, which are highly desirable for realizing efficient "magnetic reading + electric writing". Multiferroic materials which are both FE and magnetic are rare in nature due to the mutual exclusive origins of the two orders (empty d shell for conventional FE order and partially filled d shell for magnetic order). Meanwhile, for traditional multiferroics, the ME coupling is weak in type-I multiferroics with ferroelectricity and magnetism arising respectively from different mechanisms, while for type-II multiferroics where ferroelectricity is induced by magnetic ordering their spin-driven FE polarizations (mostly < 0.01 C/m2) and Curie temperature (mostly < 150 K) are far below the values for practical applications. It is the same case for previous designs of 2D type-I and type-II multiferroics.

In a new article published in the Beijing-based National Science Review, scientists at Huazhong University of Science and Technology and at the Nanjing University, China present a first-principles predictions of 2D multiferroics with robust and diversified magnetoelectric couplings: thin-layer CuCrX2 (X=S or Se).

"Theoretically, the mutual exclusion between ferroelectricity and magnetism or between high Curie temperature and strong magnetoelectricity in traditional multiferroics can be avoided here." they state in an article titled "Room-Temperature Multiferroicity and Diversified Magnetoelectric Couplings in Two-Dimensional Materials." "The vertical ferroelectricity is neither induced by empty d-shell nor spin-driven, giving rise to an alternative possibility of resolving those intrinsic exclusions and contradictions."

"Tri-layer Cu-intercalated CrX2, denoted as Cu2(CrX2)3, is still completely FM for X=Se while Cu2(CrS2)3 possesses much more complex spin configurations. Although the magnetic coupling is FM in-plane for Cu2(CrS2)3, we still need to check various possible configurations of interlayer coupling as listed in Table. S3. The FM state is higher in energy compared with three ferrimagnetic states, and the ground state turns out to be the configuration in Fig. 4(a), with a total magnetization of 2.62 μB/f.u.. When the polarization is aligned downwards, the middle layer is FM coupled with the top layer while AFM coupled with the down layer; as the polarization is reversed, according to the symmetry, the middle layer should be AFM coupled with the top layer and FM coupled with the down layer in the ground state. The energy will be lowered by 16.4 meV with the magnetization reversal of the middle layer, which should take place spontaneously considering the small barrier of spin switching equivalent to the spin anisotropy energy (<1meV). As a result, the 180-degree reversal of a considerable magnetization of 2.62 μB/f.u. can be achieved via FE switching."

"Their ferromagnetism can be stabilized due to enhanced carrier density and orbital shifting by the vertical polarization, and the Curie temperature of both ferromagnetism and ferroelectricity can be above room-temperature. Layers with different thickness may exhibit diversified types of magnetoelectrics for efficient magnetic reading + electrical writing due to the gradient of interlayer coupling parameter, where a considerable net magnetization can be reversed upon FE switching." they add. "Our prediction does not only exploit new types of multiferroic couplings in 2D, but also propose a way of constructing robust multiferroics for practical applications, which may stimulate experimental efforts concerning the recent synthesis of previously predicted intrinsic 2D ferroelectrics."


This research received funding from the National Natural Science Foundation of China.

See the article:

Tingting Zhong, Xiaoyong Li, Menghao Wu, Jun-Ming Liu
Room-Temperature Multiferroicity and Diversified Magnetoelectric Couplings in Two-Dimensional Materials
Natl Sci Rev; doi: 10.1093/nsr/nwz169

The National Science Review is the first comprehensive scholarly journal released in English in China that is aimed at linking the country's rapidly advancing community of scientists with the global frontiers of science and technology. The journal also aims to shine a worldwide spotlight on scientific research advances across China.

Disclaimer: AAAS and EurekAlert! are not responsible for the accuracy of news releases posted to EurekAlert! by contributing institutions or for the use of any information through the EurekAlert system.